China manufacturer and exporter of PTFE Xylan 1070 coated ASTM A193 B8 CL.2 Stud Bolt
What is a Xylan 1070 coated ASTM A193 B8 CL.2 Stud Bolt?
Xylan 1070 coated ASTM A193 B8 CL.2 stud bolts are high-performance fasteners manufactured from austenitic stainless steel (304 grade) with a strain-hardened process for enhanced mechanical properties. These bolts are coated with Xylan 1070, a specialized fluoropolymer-based coating, to improve corrosion resistance, chemical resistance, and durability in extreme environments.
ASTM A193 B8 CL.2 Stud Bolts are high-strength, corrosion-resistant fasteners specifically designed for high-temperature and high-pressure applications. Manufactured from 304 stainless steel and strain-hardened to meet Class 2 specifications, these stud bolts are widely used in industries such as oil & gas, chemical processing, power generation, and petrochemical.
Specifications of Xylan 1070 Coated ASTM A193 B8 CL.2 Stud Bolts:
- Standards: ASTM A193 B8 CL.2 for stud bolts and ASTM A194 grade 8 Hex nuts.
- Threads: Available in UNC, UNF, and metric thread sizes.
- Coating Thickness: Typically 20-30 microns to ensure consistent protection.
- Temperature Range: Withstands temperatures up to 250°C (482°F).
- Size range:1/4 to 4in or M6 to M100
ASTM A193 B8 CL.2 chemical composition
| Element | Composition (% by weight) |
|---|---|
| Carbon (C) | ≤ 0.08 |
| Manganese (Mn) | ≤ 2.00 |
| Phosphorus (P) | ≤ 0.045 |
| Sulfur (S) | ≤ 0.030 |
| Silicon (Si) | ≤ 1.00 |
| Chromium (Cr) | 18.00 – 20.00 |
| Nickel (Ni) | 8.00 – 11.00 |
| Nitrogen (N) | ≤ 0.10 |
ASTM A193 B8 Mechanical Properties
The mechanical properties of ASTM A193 B8 CL.2 reflect its strain-hardened condition:
| Property | Requirement |
|---|---|
| Tensile Strength | ≥ 100 ksi (690 MPa) |
| Yield Strength (0.2% offset) | ≥ 75 ksi (515 MPa) |
| Elongation in 2″ (50 mm) | ≥ 12% |
| Reduction of Area | ≥ 35% |
Hardness of ASTM A193 B8 CL.2
The hardness range for ASTM A193 B8 CL.2 is specified to ensure durability and reliability:
| Hardness | Value |
|---|---|
| Rockwell Hardness (C) | ≤ 35 HRC |
| Brinell Hardness (HBW) | ~241-321 HBW (typical) |
FAQs about Xylan 1070 Coated ASTM A193 B8 CL.2 Stud Bolts:
- What is the lifespan of Xylan 1070 coated bolts?
- The coating significantly extends the lifespan of bolts, especially in corrosive environments.
- Can Xylan 1070 bolts withstand saltwater exposure?
- Yes, Xylan 1070 provides excellent resistance to saltwater and marine conditions
You may also look for
- Xylan 1070 Coated Stud Bolt Manufacturer
- ASTM A193 B8 CL.2 Stud Bolt Supplier
- Xylan 1070 Bolt for Oil and Gas Industry
- Corrosion-Resistant Stud Bolts
-
Xylan 1070 Coated Fasteners for Marine Applications
Where to buy the Xylan 1070 Coated ASTM A193 B8 CL.2 Stud Bolts.
Name: ASME A193 B8 CL.2 Fastener
Size: 1/2 Inch
Coating: XYLAN 1070
Color: Blue
Length: 65MM
Material: ASTM A193 B8 CL2, A194 GR.8
Standard: ASME B18.31.2/B18.2.2
Note: One bolt with two Heavy Hex Nuts